(1) Chemical method
Concentrated nitric acid HN03 1000mL
Sodium chloride NaCl 40g
Temperature 65～750C
Speed ​​about 6μm/min
Precautions:
After the unqualified low-tin bronze coating is removed, the underlying metal surface is smooth and does not require polishing, but the process conditions must be strictly controlled;
2 All use concentrated nitric acid, can not have water, to prevent the substrate metal corrosion;
3 temperature can not exceed the process conditions, part of the base metal iron is corroded;
4 The chemical method can remove nickel, zinc nickel, copper, copper-tin alloy plating, etc. It is fast, low cost, and effective. Due to gas evolution, ventilation equipment is required.
(2) Electrochemical method
Triethanolamine [N(CH2CH20H)3]
60～70g/L
Sodium hydroxide (NaOH)
60～75g/L
Sodium Nitrate (NaN03)
15～20g/L
temperature
35～50°C
Anode current density
l. 5 to 2.5 A/dm2
Anode movement speed
20～25r/min
cathode
Iron or stainless steel plate
speed
About 20gm/h
Electrolytic method to remove the coating, the current should not be too large, the temperature should not be too high to prevent the corrosion of the base metal iron.
Slotted Nuts
Product categories of Slotted Nuts, we are specialized manufacturers from China, Castellated Nut, Slotted Round Nuts suppliers/factory, wholesale high-quality products of Slotted Hex Nuts R & D and manufacturing, we have the perfect after-sales service and technical support. Look forward to your cooperation!
Slotted Nuts,Nuts Screws,Hexagon K Nuts,Open End Rivet Nut,Carbon Steel Flat Head Rivet Nut
Suzhou Gubao Screws Co.,Ltd. , https://www.gbscrewes.com